双壁复合热缩套管由外半导层和内绝缘层构成,该产品通过共同挤出形成,两层之间有良好的结合,无缝隙,收缩前后两层之间可以共呼吸.主要适用于10KV及36KV以上电缆的连接。 *标准包装长度为1000mmm。 性能参数 | Sr | Property | Test Method | Typical Value | | 外半导层 | | | | 1 | 密度 | ASTM D792 | 1.0 | | 2 | 拉伸强度 | ASTM D412 | 12 N/mm2 | | 3 | 断裂伸长率 | ASTM D412 | 300% | | 4 | 吸水率 | ASTM D570 | < 0.5% | | 内绝缘层 | | 1 | 密度 | ASTM D792 | 1.0 | | 2 | 拉伸强度 | ASTM D412 | 15 N/mm2 | | 3 | 断裂伸长率 | ASTM D412 | 350% | | 4 | 吸水率 | ASTM D570 | < 0.5% | | 5 | 体积电阻系数 | ASTM D257 | 1 x 1014Ω.cm | Finished product | | 1 | 热冲击 @ 200℃ | ASTM D2671 | Passes | | 2 | 低温柔韧性@ -20℃ | ASTM D2671 | Passes | | 3 | 纵向改变 | ASTM D2671 | Inside 10% | | 4 | Wallthicknessratio | ASTM D2671 | > 0.6 | | | | | |
| 尺寸和适用范围 | | 规格 | 收缩前内径(mm) | 收缩后内径(mm) | 完全收缩后壁厚(mm) | | DW 35/12 | 35 | 12 | 6.00 | | DW 45/15 | 45 | 15 | 6.00 | | DW 55/18 | 55 | 18 | 6.00 | | DW 65/25 | 65 | 25 | 6.50 | | DW 85/30 | 85 | 30 | 6.50 | | DW100/38 | 100 | 38 | 6.50 | | DW120/45 | 120 | 45 | 7.00 | | DW140/50 | 140 | 50 | 7.00 |
|